SABIC® PPcompound 7996
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | t0b1AZ_SABIC-PPcompound-7996.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPcompound 7996 is a modified mineral filled Polypropylene for automotive exterior applications. The material combines high flow, very high stiffness, good scratch resistance and an excellent UV performance. The combination of a broad processing window and good mechanical properties and the UV resistance make it suited for demanding aesthetic automotive exterior applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 30 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 150 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 67 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20mm | 26.0 | MPa | ISO 527-2/5/50 |
| Fracture, 3.20mm | 20.0 | MPa | ISO 527-2/5/50 |
| Tensile Strain (Break, 3.20 mm) | 40 | % | ISO 527-2/5/50 |
| Flexural Modulus 1 | 2000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (-40°C) | 15 | kJ/m² | ISO 179 |
| Notched Izod Impact | ISO 180/3A | ||
| -20°C | 2.3 | kJ/m² | ISO 180/3A |
| 0°C | 3.0 | kJ/m² | ISO 180/3A |
| 23°C | 5.0 | kJ/m² | ISO 180/3A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 120 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 140 | °C | ISO 306/A50 |
| CLTE - Flow | 9.5E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Mold Shrinkage, SABIC Method: 0.9% |
| Note Message | |
|---|---|
| 1 . | Method I (three-point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-6462 | Ravago Manufacturing Americas, LLC | PP Homopolymer | Ravago Compounds |
| Multi-Flex® TPO 2503 S | Multibase, A Dow Corning Company | TPO (POE) | Multi-Flex® TPO |
| Daelim Po1y® PP-247 | DAELIM INDUSTRIAL CO., LTD. | PP Impact Copolymer | Daelim Po1y® |
| Lifolit® E 73.1340/2 glasklar | ELASTO | PVC, Flexible | Lifolit® |
| LNP™ THERMOCOMP™ 2C003 compound | SABIC Innovative Plastics | ETFE | LNP™ THERMOCOMP™ |