Huafon EP158 Datasheet,Nylon 66,Huafon Group Co., Ltd.-SHANGHAI SUSHENG

Huafon EP158

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Huafon Group Co., Ltd.
Trademark:	Huafon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	t08TuE_Huafon-EP158.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
EP158 is a general purpose Nylon 66 resin. This resin offers a well-balanced combination of engineering properties characterized by high strength: good toughness; high impact; good surface lubricity: abrasion resistance; resistant low temperature: self-extinguishment. Typical Applications EP158 is suitable for compounding and injection molding, also widely used in spinning monofilament, staple. Terminal applications mainly in machinery, electronics, electrical, instrumentation, automotive components, railway, home appliances, communications, textile, oil pipe/tank and precision engineering products, etc., EP158 also can be used for the production of film, packing, medical equipment, sporting goods, and daily necessities and so on.

Message

EP158 is a general purpose Nylon 66 resin. This resin offers a well-balanced combination of engineering properties characterized by high strength: good toughness; high impact; good surface lubricity: abrasion resistance; resistant low temperature: self-extinguishment.

Typical Applications
EP158 is suitable for compounding and injection molding, also widely used in spinning monofilament, staple. Terminal applications mainly in machinery, electronics, electrical, instrumentation, automotive components, railway, home appliances, communications, textile, oil pipe/tank and precision engineering products, etc., EP158 also can be used for the production of film, packing, medical equipment, sporting goods, and daily necessities and so on.

General Information
Features	General Purpose Good Abrasion Resistance Good Toughness High Impact Resistance High Strength Low Temperature Resistant Self Extinguishing
Uses	Appliances Automotive Applications Compounding Electrical/Electronic Applications Engineering Parts Film General Purpose Medical Devices Monofilaments Packaging Piping Sporting Goods Tanks Telecommunications Textile Applications
Appearance	Clear/Transparent
Processing Method	Compounding Fiber (Spinning) Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (275°C/2.16 kg)	71	g/10 min	ISO 1133
Particle Size	1.40 to 2.00	g/100 pellets	Internal Method
Relative Viscosity	2.62 to 2.72		Internal Method
Water Content	< 5000	mg/kg	Internal Method

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress ¹	75.3	MPa	ISO 527-2
Tensile Strain ²(Break)	70	%	ISO 527-2
Flexural Modulus ³	2660	MPa	ISO 178
Flexural Stress ⁴	99.6	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength ⁵(23°C)	6.1	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature ⁶
0.45 MPa, Annealed	186	°C	ISO 75-2/B
1.8 MPa, Annealed	67.4	°C	ISO 75-2/A
Vicat Softening Temperature ⁷	240	°C	ISO 306/B120
Peak Melting Temperature ⁸	268	°C	ASTM D3418

Flammability	Nominal Value	Test Method
Flame Rating ⁹		UL 94
1.00 mm	V-2
1.60 mm	V-2
3.00 mm	V-2

Note Message
1 .	48h/23°C/50%RH
2 .	48h/23°C/50%RH
3 .	48h/23°C/50%RH
4 .	48h/23°C/50%RH
5 .	48h/23°C/50%RH
6 .	48h/23°C/50%RH
7 .	48h/23°C/50%RH
8 .	10°C/min
9 .	48h/23°C/50%RH

Resin Grade	Manufacturer	Category	Trademark
Radilon® S ESL128 100 NAT	Radici Plastics	Nylon 6	Radilon®
Hapflex™ 1056	Hapco Inc.	TP, Unspecified	Hapflex™
LONGLITE® PBT 7030-104X	CCP Group	PBT+ASA	LONGLITE® PBT
Magnobond 87	Magnolia Plastics, Inc.	Epoxy	Magnobond
Sumikon® PM-TX250	SBHPP	Phenolic	Sumikon®