| Vyncolit® X7012 is a glass fiber and glass beads reinforced molding compound with high mechanical strength, even at high temperatures in Long Life Coolants. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | ISO 1183 |
| Apparent Density | 0.64 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.35 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ISO 62 |
| Post Shrinkage | 0.090 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.6 | % | ISO 178 |
| Tensile Modulus (Injection Molded) | 13000 | MPa | ISO 527-2 |
| Tensile Stress (Break, Injection Molded) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 0.80 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 12000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 190 | MPa | ISO 178 |
| Compressive Stress | 260 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 3.8 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (Injection Molded) | 13 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 213 | °C | ISO 75-2/Af |
| CLTE | TMA | ||
| Flow | 1.9E-5 | cm/cm/°C | |
| Transverse | 5.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.9E+13 | ohms | IEC 60093 |
| Volume Resistivity | 7.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 17 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 6415-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Multilon® DN-3720F | TEIJIN LIMITED | PC+ABS | Multilon® |
| ALCOM® PA66 910/1 GF30 PTFE15 SI2 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| INSPIRE™ TF1500 ESU | Trinseo | TPO | INSPIRE™ |
| Karina MB CONC DE PIGM. BLUE -E 06/815-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |