EOS PA 2200 Top Speed 1.0

Category:	Nylon 12 , Polyamide 12
Manufacturer:	EOS GmbH
Trademark:	EOS
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	sypUX3_EOS-PA-2200-Top-Speed-1-0.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

This whitish fine powder PA 2200 on the basis of polyamide 12 serves with its very well-balanced property profile a wide variety of applications. Laser-sintered parts made from PA 2200 possess excellent material properties:

high strength and stiffness

good chemical resistance

excellent long-term constant behaviour

high selectivity and detail resolution

various finishing possibilities (e.g. metallisation, stove enamelling, vibratory grinding, tub colouring, bonding, powder coating, flocking)

bio compatible according to EN ISO 10993-1 and USP/level VI/121 °C

approved for food contact in compliance with the EU Plastics Directive 2002/72/EC (exception: high alcoholic foodstuff)

Typical applications of the material are fully functional plastic parts of highest quality. Due to the excellent mechanical properties the material is often used to substitute typical injection moulding plastics. The biocompatibility allows its use e.g. for prostheses, the high abrasion resistance allows e.g. the realisation of movable part connections.

180 µm layer thickness:
TopSpeed is a very economical parameter set for parts with medium to high requirements of quality and mechanical load and high cost pressure. Particularly large and relatively thick-walled parts can usually profit from this layer thickness, mostly without any noticeable impairment from the fast build-up rates.

General Information
Features	Biocompatible Food Contact Acceptable Good Abrasion Resistance Good Chemical Resistance High Stiffness High Strength
Uses	Medical/Healthcare Applications Prosthetics Prototyping Thick-walled Parts
Agency Ratings	EU 2002/72/EC ISO 10993 USP Class VI
Appearance	White
Forms	Powder
Processing Method	3D Printing, Laser Sintering/Melting

Physical	Nominal Value	Unit	Test Method
Density	0.930	g/cm³	Internal Method
Thickness - Layer	180.0	µm

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, 15 sec)	75		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus ¹	1500	MPa	ISO 527-2
Tensile Stress
-- ²	38.0	MPa	ISO 527-2
-- ³	45.0	MPa	ISO 527-2
Tensile Strain
Break ⁴	18	%	ISO 527-2
Break ⁵	3.0	%	ISO 527-2
Flexural Modulus ⁶(23°C)	1500	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength ⁷(23°C)	4.8	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength ⁸(23°C)	53	kJ/m²	ISO 179/1eU
Notched Izod Impact Strength (23°C)	4.4	kJ/m²	ISO 180/1A

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	163	°C	ISO 306/B50
Melting Temperature	176	°C	ISO 11357

Note Message
1 .	X Direction
2 .	Z Direction
3 .	Y Direction
4 .	X Direction
5 .	Z Direction
6 .	X Direction
7 .	X Direction
8 .	X Direction

Resin Grade	Manufacturer	Category	Trademark
YUPLENE® R151A	SK Global Chemical	PP Random Copolymer	YUPLENE®
Akulon® F230-C	DSM Engineering Plastics	Nylon 6	Akulon®
ELASTOSIL® P 7684/60 A/B	Wacker Chemie AG	Silicone	ELASTOSIL® P
Petroquim PP PH 0322	Petroquim S.A.	PP Homopolymer	Petroquim PP
REV Materials 8006-002	REV Materials	PP, Unspecified	REV Materials