Baytec® RTC V85 Component A (99\33\62\5)
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | swtvbC_Baytec-RTC-V85-Component-A-99-33-62-5-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec RTC-V85 Component A is a four component, 100%-solid rotational casting system, which can make urethane elastomers in a range of hardness (72 to 93 Shore A). The isocyanate component is a modified diphenylmethane diisocyanate (MDI) prepolymer, and the three polyol components are polyether polyol blends. The system is a special, fast reacting system designed to be cast on rotating roll cores using the rotational casting technique. Typical applications are on rolls for the paper, textile, and steel industries and belt rollers. This system can be pigmented to most any color. As with any product, use of the Baytec RTC-V85 Component A in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240 | |
| Hardness- Pusey & Jones | 27.0 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compression Deflection - 25% | 4.45 | MPa | ASTM D575 |
| Taber Abrasion Resistance (1000 Cycles) | 200 | mg | ASTM D4060 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 17.1 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 460 | % | ASTM D412 |
| Tear Strength 1 | 64.8 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components | |||
| Part C | Mixing ratio by weight: 62 | ||
| Part D | Mixing ratio by weight: 5.0 | ||
| Component a | Mixing ratio by weight: 99 | ||
| Component B | Mixing ratio by weight: 33 |
| Additional Information |
|---|
| Part A Type: Isocyanate Appearance: Yellowish liquid Specific Gravity @ 25°C: 1.09 Viscosity @25°C: 2000 to 3000 mPa Flash Point, PMCC: 216°C NCO: 9.65 to 10.24 wt% Part B Type: Polyol Appearance: White liquid Specific Gravity @ 25°C: 1.03 Viscosity @25°C: 1500 mPa-s Flash Point, PMCC: 165°C Hydroxyl Number: 68 mg KOH/g Part C Type: Polyol Appearance: White liquid Specific Gravity @ 25°C: 1.04 Viscosity @25°C: 2200 mPa-s Flash Point, PMCC: 165°C Hydroxyl Number: 148 mg KOH/g Part D Type: Polyol Appearance: White liquid Specific Gravity @ 25°C: 1.03 Viscosity @25°C: 1300 mPa-s Flash Point, PMCC: 177°C Hydroxyl Number: 177 mg KOH/g |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE F0863 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| UBE Polyethylene B028 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| NEOFLON™ ACX-31 | DAIKIN AMERICA, INC. | PFA | NEOFLON™ |
| Hifax HSBM CB 1157 BLACK | LyondellBasell Industries | PP Copolymer | Hifax |
| Sylvin 8749-80AM Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |