YUCLAIR® JL210
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SK Global Chemical |
| Trademark: | YUCLAIR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | swFYh2_YUCLAIR-JL210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| YUCLAIR JL210 is linear low density polyethylene resin for general injection molding application. It offers excellent processability and flexibility. This resin is particularly suitable for the production of lids. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 52 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 245 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength - MD | ASTM D882 | ||
| Yield | 14.7 | MPa | |
| Break | 11.8 | MPa | |
| Tensile Elongation - MD (Break) | 600 | % | ASTM D882 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 19HT60-0.002 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| Aropol™ Q 67700 resins | Ashland Performance Materials | Polyester, TS | Aropol™ |
| Daelim Po1y® LH-6050 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Electrafil® 99054 | Techmer Engineered Solutions | PP Copolymer | Electrafil® |
| Polifil® Nylon 628-13GF | The Plastics Group | Nylon 66 | Polifil® Nylon |