AMPAL® MPV 7270
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | RASCHIG GmbH |
| Trademark: | AMPAL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | suAgep_AMPAL-MPV-7270.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Inorganically filled melamine-modified Polyester moulding compound Low post-shrinkage and distortion tendencies, very good electrical values, excellent surface quality and dimensional stability at elevated temperatures Moulded parts in electrical engineering, Fittings for household appliances, Car ash-trays This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 to 1.80 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 to 1.00 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow | ISO 2577 | ||
| -- 1 | 0.50 to 0.80 | % | |
| -- 2 | 0.70 to 1.0 | % | |
| Water Absorption (23°C, 24 hr) | < 1.0 | % | ISO 62 |
| Post Shrinkage 3 | 0.20 to 0.40 | % | ISO 2577 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature | IEC 60216 | ||
| <50 h | 190 | °C | |
| 20,000 h | 150 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 10.0 | MPa | |
| Compression Molding Temperature | 160 to 180 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| Compression Molded | 4000 to 6000 | MPa | |
| Injection Molded | 5000 to 7000 | MPa | |
| Tensile Stress | ISO 527-2 | ||
| Compression Molded | 30.0 to 50.0 | MPa | |
| Injection Molded | 50.0 to 60.0 | MPa | |
| Flexural Modulus | ISO 178 | ||
| Compression Molded | 8000 to 9000 | MPa | |
| Injection Molded | 8000 to 9000 | MPa | |
| Flexural Stress | ISO 178 | ||
| Compression Molded | 70.0 to 90.0 | MPa | |
| Injection Molded | 90.0 to 110 | MPa | |
| Compressive Stress | 150 to 200 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| Compression Molded | 1.5 to 2.5 | kJ/m² | |
| Injection Molded | 1.5 to 2.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| Compression Molded | 8.0 to 10 | kJ/m² | |
| Injection Molded | 10 to 12 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 180 to 200 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 80.0 to 110 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 100°C) | 2.0E-5 to 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.50 to 0.60 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 to 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 to 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 to 40 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 7.00 5.00 | ||
| 1 MHz | 5.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.10 to 0.20 | ||
| 1 MHz | 0.030 to 0.050 | ||
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Tested by RASCHIG) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Middle Temperature | 50.0 to 75.0 | °C | |
| Front Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 100 to 115 | °C | |
| Mold Temperature | 165 to 180 | °C | |
| Back Pressure | 0.800 to 1.20 | MPa | |
| Screw Speed | 80 to 120 | rpm |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | Injection Molded |
| 3 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solarkote® P-611 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Solarkote® |
| LGSTRENE LGG 102 | LG Polymers India Pvt. Ltd. | PS (GPPS) | LGSTRENE |
| Pacrel® 5355N | Nanjing Jinling OPTA Polymer Co., Ltd. | TPE | Pacrel® |
| Sumiliteresin® PR-14170 | SBHPP | Phenolic | Sumiliteresin® |
| Sylvin 2990-90 Clear 8436 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |