MAJORIS FW214 - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | stcMgY_MAJORIS-FW214---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FW214 - 8229 is a 20% glass/mineral reinforced polypropylene compound intended for injection moulding. The product is available in both black (FW214 - 8229) and natural (FW214) but other colours can be provided on request. FW214 - 8229 has been developed especially for the automotive applications and electrical components. APPLICATIONS Products requiring very good long term heat resistance, high heat distortion temperature, excellent rigidity, low shrinkage and high dimensional stability can suitably be made from FW214 - 8229.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 51.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 129 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 270 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex A0520FN N3 | Ginar Technology Co., LTD. | Nylon 6 | Mapex |
| Maxxam™ PPH-20C Nat | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Raditer® B RV200 | Radici Plastics | PBT | Raditer® |
| ALFATER XL® A40I 2GP0050 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Karina WHITE COLOR CONCENTRATE 10/1-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |