Order Products : sales@su-jiao.com
Diakon® Frost 952 51
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Inc. |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | st2BZO_Diakon-Frost-952-51.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Diakon®Frost 952 51 is a polymethyl methacrylate-acrylic material,. This product is available in Europe and is processed by extrusion or injection molding. Diakon®The main characteristics of Frost 952 51 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 1.3 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 94 | ISO 2039-2 | |
| Ball Indentation Hardness (H 961/30) | 180 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 73.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 3400 | MPa | ISO 178 |
| Flexural Stress | 103 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.4 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 10 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 1.6 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 109 | °C | ISO 306/A |
| -- | 102 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 74.0 | % | ASTM D1003 |
| Haze | 66 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 50.0 - 80.0 | °C | |
| Cylinder Zone 1 Temp. | 160 - 240 | °C | |
| Cylinder Zone 2 Temp. | 180 - 250 | °C | |
| Cylinder Zone 3 Temp. | 200 - 250 | °C | |
| Cylinder Zone 4 Temp. | 220 - 260 | °C | |
| Adapter Temperature | 210 - 270 | °C | |
| Die Temperature | 210 - 270 | °C |
| Extrusion instructions |
|---|
| Vent Zone: 220 to 270°CZone 6: 220 to 270°CZone 7: 210 to 270°CZone 8: 210 to 270°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 5061 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Spartech Polycom 2946-96A | Spartech Polycom | PVC, Unspecified | Spartech |
| CERTENE™ PRB-2C | Muehlstein | PP Random Copolymer | CERTENE™ |
| LNP™ THERMOCOMP™ RX10405H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| LUVOCOM® 1106-8664/L | LEHVOSS Group | PEI | LUVOCOM® |