Lion Idemitsu Composites PPS Y551F1
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | Lion Idemitsu Composites PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ssg6V6_Lion-Idemitsu-Composites-PPS-Y551F1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lion Idemitsu Composites PPS Y551F1 is a Polyphenylene Sulfide (PPS) product filled with 50% mineral. It is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.89 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.70 | % | |
| Flow | 0.40 | % | |
| Water Absorption (23°C, 24 hr) | > 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 93 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 77.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.80 | % | ISO 527-2 |
| Flexural Modulus | 16300 | MPa | ISO 178 |
| Flexural Stress | 137 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 2.9 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 222 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 1.6E-5 | cm/cm/°C | |
| Transverse | 3.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Electric Strength | IEC 60243-1 | ||
| 1.00 mm | 29 | kV/mm | |
| 3.00 mm | 13 | kV/mm | |
| Dielectric Constant | 3.90 | IEC 60250 | |
| Dissipation Factor | 1.2E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flowability 2(1.00 mm) | 115 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | Internal Method |
| 2 . | Thickness 1mm, Cylinder temperature 320°C, Injection pressure 100MPa, Mold temperature 135°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP PHC28 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| Starflam PX05004 | Eurostar Engineering Plastics | Nylon 66/6 | Starflam |
| TAROMID B 280 G3 X0 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| TOTAL Polyethylene HDPE 56020 S XP | TOTAL Refining & Chemicals | HDPE, UHMW | TOTAL Polyethylene |
| Shida 030E-1 | JINJIANG City SHIDA Plastic Fine Co., Ltd. | SBS | Shida |