INSULCAST® RTVS 8127
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® RTVS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sq8hAG_INSULCAST-RTVS-8127.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST RTVS 8127 is a: flame retardant, reversion resistant silicone compound. The low viscosity and high thermal conductivity makes the RTVS 8127 ideal for potting dense component packages requiring heat dissipation. This compound has excellent thermal stability, electrical properties, is compatible with most electrical insulating materials and has a UL 94 Flame Rating of 94 V-0. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 50 to 60 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 2.90 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 120 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 1.8E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.75 | W/m/K | |
| Service Temperature | -55 to 204 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.00 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 5.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Colorless | ||
| -- 2 | Grey | ||
| Density | |||
| -- 3 | 1.78 | g/cm³ | |
| -- 4 | 1.78 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| 25°C 5 | 3.0 | Pa·s | |
| -- 6 | 4.0 | Pa·s | |
| 25°C 7 | 5.0 | Pa·s | |
| Curing Time | |||
| 120°C | 0.25 | hr | |
| 95°C | 0.50 | hr | |
| 60°C | 2.0 | hr | |
| 25°C | 24 | hr | |
| Pot Life 8(25°C) | 30 to 60 | min |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | Part B |
| 4 . | Part A |
| 5 . | Part B |
| 6 . | Mixed |
| 7 . | Part A |
| 8 . | 100 gram mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riblene® FF 20 | Versalis S.p.A. | LDPE | Riblene® |
| THERMOLAST® K TC5FRN (Series: FR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Fainplast PVC FK 93 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Elastron® G G500.A50.N.ABS | Elastron USA, Inc. | SEBS | Elastron® G |
| LNP™ STAT-KON™ QEL329 compound | SABIC Innovative Plastics Asia Pacific | Nylon 610 | LNP™ STAT-KON™ |