YUCLAIR® FV149M
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SK Global Chemical |
| Trademark: | YUCLAIR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | spqpfg_YUCLAIR-FV149M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
YUCLAIR FV149M is butene-1 copolymer designed for use in general purpose film application. YUCLAIR FV149M provides stronger film than ones made from competitive LLDPE film grades. Therefore YUCLAIR FV149M shows superior tensile strength, tear strength, gel-free, antiblock and sealibility. Outstanding clarity and good processibility make this resin an ideal choice for film application when blended with conventional LDPE. YUCLAIR FV149M can be processed readily into blown film using standard extrusion techniques. YUCLAIR FV149M complies with FDA regulations in 21 CFR177.1520 for all food contact. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | ASTM D746 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 11.8 | MPa | ASTM D882 |
| TD : Yield, 50 µm | 10.8 | MPa | ASTM D882 |
| MD : Break, 50 µm | 37.3 | MPa | ASTM D882 |
| TD : Break, 50 µm | 34.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 790 | % | ASTM D882 |
| TD : Break, 50 µm | 870 | % | ASTM D882 |
| Spencer Impact (50.0 µm) | 0.785 | J | ASTM D3420 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ASTM D1922 | ||
| MD : 50.0 µm | 29.4 | kN/m | ASTM D1922 |
| TD : 50.0 µm | 78.5 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm) | 23 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 190 | °C | |
| Die Temperature | 190 - 195 | °C |
| Extrusion instructions |
|---|
| Film Extrusion Condition: Screw dia 50, Die dia 150, BUR 2.2Die gap 1.8, Screw RPM 45, L/S 7.2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® 70G33L NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| HiFill® ASA GF15 | Techmer Engineered Solutions | ASA | HiFill® |
| HiFill FR® PP CO FR HS | Techmer Engineered Solutions | PP Copolymer | HiFill FR® |
| KANEKA H516A | Kaneka North America LLC | CPVC | KANEKA |
| EPALINE 386A55 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPALINE |