TARFLON™ NEO VG2240
| Category: | PC , Polycarbonate |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | TARFLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | soklMO_TARFLON-NEO-VG2240.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Weather resistance |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 8.00 | cm³/10min | ISO 1133 |
| Spiral Flow | 20.0 | cm | Internal Method |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 2.00 mm | 0.60 to 0.80 | % | |
| Flow : 2.00 mm | 0.60 to 0.80 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 100 | % | ISO 527-2 |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Flexural Stress | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 75 | kJ/m² | |
| 0°C | 85 | kJ/m² | |
| 23°C | 90 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 750 | J/m | |
| 0°C | 800 | J/m | |
| 23°C | 850 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 139 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | >PC< |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature | 270 to 310 | °C | |
| Middle Temperature | 270 to 310 | °C | |
| Front Temperature | 270 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 24h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POYAD CR207I | Pooya Polymer Tehran | PE, Unspecified | POYAD |
| MOSTEN FT 005 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| Braskem PP DS6D21 | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| GAPEX® RPP30EA52WH | Ferro Corporation | PP, Unspecified | GAPEX® |
| Hypro® PPH-CC30 NATURAL | Entec Polymers | PP Homopolymer | Hypro® |