INSPIRE™ TF1500SC
| Category: | TPO , Performance Polymers |
| Manufacturer: | Trinseo |
| Trademark: | INSPIRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | soMg9i_INSPIRE-TF1500SC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High impact talc filled natural PP compounded developed for covered interior automotive applications. Can also be used for self-colouration (SC) in combination with PROMATCH™ combi-masterbatches. INSPIRE™ TF1500 SC combines excellent processing and high impact performance. It is intended for applications requiring good balance between toughness and stiffness. Applications
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 - 1.2 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1950 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 70 | % | ISO 527-2/50 |
| Flexural Modulus | 1850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| 0°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 15 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy 1(23°C, 3.00 mm) | 70.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 58.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306/A120 |
| CLTE - Flow (-30 to 23°C) | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Additional Information |
|---|
| The information and data contained herein is specific to the natural (neat) product. For properties of the material in combination with PROMATCH* combi masterbatches (PP Combi Masterbatch CMPP 10.22 and CMPP 10.23) please refer to the technical data sheet for INSPIRE* TF1500 ESU. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Energy to Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom EP6333 B1 | Spartech Polycom | PP, Unspecified | Spartech |
| Nypol® PA B3 HL HV400 NTLA010 NT389 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Fluoroplex F 25 - GMP | UNIFLON | PTFE | Fluoroplex |
| Grupo IDESA HIPS HI-730-S-01 | Grupo IDESA, S.A. de C.V. | SBC | Grupo IDESA HIPS |
| Karina WHITE PVC COMPOUND -E 851-10/ 1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |