POCAN® BFN 4231 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sn0xpW_POCANBFN4231000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 25 % glass fibers, injection molding, halogen free flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.52 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 40.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 260°C, 2.00mm 1 | 1.2 | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.10 | % | ISO 294-4 |
| Flow direction : 260°C, 2.00mm 3 | 0.50 | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.10 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 10500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 10000 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 165 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 2.4 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT, GFHMR, 09-110, GF25; ISO 1043-PBT GF FR(30+40) | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 35 | kJ/m² | ISO 179/1eU |
| 23°C | 40 | kJ/m² | ISO 179/1eU |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 33 | kJ/m² | ISO 180/1U |
| 23°C | 36 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 224 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 206 | °C | ISO 306/B50 |
| Ball Pressure Test (214°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 8 | 220 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 2.3E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 35 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-0 | UL 94 | |
| 0.750 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 5VA | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.400 mm | 960 | °C | IEC 60695-2-12 |
| 0.750 mm | 960 | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.400 mm | 850 | °C | IEC 60695-2-13 |
| 0.750 mm | 775 | °C | IEC 60695-2-13 |
| 1.50 mm | 825 | °C | IEC 60695-2-13 |
| 3.00 mm | 850 | °C | IEC 60695-2-13 |
| Oxygen Index 9 | 44 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66/6 CF 30 | Plastcom | Nylon 66/6 | SLOVAMID® 66/6 |
| Sylvin 8329-75LG Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ChronoThane™ P 80A | CardioTech International, Inc. | PUR-MDI | ChronoThane™ |
| GPPC ABS D-1000S | GPPC Chemical Co., Ltd. | ABS | GPPC ABS |
| LOXIM 810 02T HB | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |