Clariant Nylon 6/6 66G25M15
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant Nylon 6/6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | smgWOF_Clariant-Nylon-6-6-66G25M15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Clariant Nylon 6/6 66G25M15 is a Polyamide 66 (Nylon 66) material filled with 25% glass fiber and 15% mineral. It is available in North America for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 7650 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 238 | °C | ASTM D648 |
| Melting Temperature | 261 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 271 to 288 | °C | |
| Front Temperature | 282 to 299 | °C | |
| Nozzle Temperature | 266 to 288 | °C | |
| Mold Temperature | 71.1 to 104 | °C | |
| Injection Pressure | 55.2 to 138 | MPa | |
| Back Pressure | 0.00 to 1.03 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melochem 791 | Chemiplastica, Inc. | Mel Formald | Melochem |
| Franprene TGA 2255RY | Franplast S.r.l. | SBS | Franprene |
| KMI PBS KM802A | KMI Group Inc. | PBS | KMI PBS |
| Lifoflex® UV 40 GB 1040 | ELASTO | SEBS | Lifoflex® |
| KMI PP KM-199IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |