FHR Polypropylene P4C6B-194
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Flint Hills Resources, LP |
| Trademark: | FHR Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | siHcUZ_FHR-Polypropylene-P4C6B-194.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DESCRIPTION: Homopolymer FEATURES: Antistat, Nucleated. Produced without animal derived components or phthalates. APPLICATIONS: Injection Molding REGULATORY: FDA - 21 CFR 177.1520(c)1.1a |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 36.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 9.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant | 1400 | MPa | |
| Tangent | 1480 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 | J/m | ASTM D256 |
| Gardner Impact (23°C) | 6.00 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 109 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPC364I6 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| SITRAROY 30E-V0 / C7035 grau | SITRAPLAS GmbH | ASA+PC | SITRAROY |
| SLOVALEN® PH 78 FRT 5 | Plastcom | PP, Unspecified | SLOVALEN® |
| TRIBIT® 1500G20K | Samyang Corporation | PBT | TRIBIT® |
| EXCELLOY CZ500 | Techno Polymer Co, Ltd. | PC+ABS | EXCELLOY |