Retpol® 7517 UV3 SAS
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | shEteu_Retpol-7517-UV3-SAS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Epalex 7517 UV3 SAS is a thermoplastic rubber modified mineral filled polypropylene compound. It is a very high flow injection moulding grade developed for parts with long flow lengths and high impact strength at sub-zero temperatures whilst maintaining good rigidity at high ambient temperatures. The material displays minimal shrinkage and low CLTE. It contains an antistatic agent and mould release and is stabilized for continuous outdoor weathering. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.50 to 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 41 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 67 | ||
| Shore D, 15 sec, 3.00 mm | 56 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 17.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 350 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 1670 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.00 mm | 240 | J/m | |
| 0°C, 3.00 mm | 410 | J/m | |
| 23°C, 3.00 mm | 540 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.00 mm) | 102 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Royalite R104 | Spartech Plastics | ABS | Royalite |
| NEFTEKHIM PP 4210G (EP2S30B) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Borealis PP ZP961 | Borealis AG | TPO | Borealis PP |
| TECACOMP® PA66 CF20 black 4102 | Ensinger GmbH | Nylon 66 | TECACOMP® |
| TECHNYL STAR® S 60G1 V30 NATURAL LP | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |