CERTENE™ PHF-8E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sgt6Pc_CERTENE-PHF-8E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PHF-8E is a certified prime grade Polypropylene specially designed for non-oriented Tubular Film EXTRUSON by Water Quench - TQ - process. PHF-8E combines excellent processability and good melt thermal stability, with films exhibiting sparkling clarity, good impact strength, easy open ability, stiffness, good barrier to fats and oils, and good chemical resistance. PHF-8E applications include film for articles requiring excellent see-through clarity such as textiles, soft goods and pastries, pre-cooked foods sterilizable bags, bags to pack cooked foods, and wrapping paper products. PHF-8E contains high slip and medium antiblock, and its recommended processing temperature is between 210° to 230°C. PHF-8E complies with FDA regulation 21CFR 177.1520 (a)(1) (b) (c)1.1, and most international regulations concerning Polypropylene use in contact with food articles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.907 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus - 1% Secant (Injection Molded) | 1550 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus 1 | ASTM D882 | ||
| 1% Secant, MD : 32 µm | 689 | MPa | |
| 1% Secant, TD : 32 µm | 689 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Break, 32 µm | 55.2 | MPa | |
| TD : Break, 32 µm | 37.9 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break, 32 µm | 500 | % | |
| TD : Break, 32 µm | 550 | % | |
| Elmendorf Tear Strength 4 | ASTM D1922 | ||
| MD : 32 µm | 40 | g | |
| TD : 32 µm | 40 | g | |
| Spencer Impact 5(31.8 µm) | 400 | g | ASTM D3420 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 6(45°, 31.8 µm) | 85 | ASTM D2457 | |
| Haze 7(31.8 µm) | 2.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 2 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 3 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 4 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 5 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 6 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 7 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 TFE 2 DEL | RTP Company | Acetal (POM) Homopolymer | RTP |
| VICOTE® 705 Blue | Victrex plc | PEEK | VICOTE® |
| Ultraform® N 2640 Z6 | BASF Corporation | Acetal (POM) Copolymer+PUR | Ultraform® |
| Ad-Tech Epoxy CTC-110 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| FRAGOM PR/04 AFKK N | Crosspolimeri S.p.A. | TP, Unspecified | FRAGOM |