Riblene® AB 10
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sfNSnp_RibleneAB10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene AB 10 is a high molecular weight low density polyethylene resin (LDPE) suitable for blown film extrusion. Riblene AB 10 is characterized by a high melt strength leading to a good bubble stability during extrusion. Films manufactured by Riblene AB 10 are easily heat shrinkable and characterized by optimum mechanical properties. Main Applications Riblene AB 10 is recommended for the production of greenhouse film, heavy duty shrink film and industrial bags. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.15 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.60 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Dynamic, Blown Film) | > 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 70 | µm | |
| Film Thickness - Recommended / Available | 60 to 250 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% sectioning, MD : 70 µm | 150 | MPa | ISO 527-3 |
| 1% sectioning, TD : 70 µm, blown film | 180 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : yield, 70 µm, blow film | 9.00 | MPa | ISO 527-3 |
| TD : yield, 70 µm, blow film | 9.00 | MPa | ISO 527-3 |
| MD : broken, 70 µm, blown film | 27.0 | MPa | ISO 527-3 |
| TD : broken, 70 µm, blown film | 25.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : broken, 70 µm, blown film | 400 | % | ISO 527-3 |
| TD : broken, 70 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (70 µm, Blown Film) | 380 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 70 µm, blown film | 25 | N | ISO 6383-2 |
| TD : 70 µm, blown film | 35 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 91.0 | °C | ISO 306/A |
| Melting Temperature | 109 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 70.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (70.0 µm, Blown Film) | 12 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VALOX™ 4031 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| Fainplast PVC RH 210/W | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Kumho KNB 3430G | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |
| INLUBE INX-SAN-09055 | Infinity LTL Engineered Compounds | SAN | INLUBE |
| OXNILON 66 30CF 15PTFE | Oxford Polymers | Nylon 66 | OXNILON 66 |