Allen ABS 552
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SEKISUI Polymer Innovations, LLC |
| Trademark: | Allen ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sef6oV_Allen-ABS-552.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
552 is a general purpose ABS with medium impact and a medium gloss finish. Common Applications:
Features and Benefits:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 35.9 | MPa | ASTM D638 |
| Flexural Modulus | 2000 | MPa | ASTM D790 |
| Flexural Strength | 59.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -18°C | 130 | J/m | |
| 23°C | 260 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 93.3 | °C | |
| 1.8 MPa, Unannealed | 87.8 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 50 to 70 | ASTM D523 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Dynaprene® VE5073A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Elastron® G G400.A65.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina BLACK PVC COMPOUND 830-48/1 1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PermaStat® 2503 | RTP Company | PC+ABS | PermaStat® |
| Sarlink® TPE FM-2676 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |