ALCUDIA® LDPE 2203F
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | seRsrk_ALCUDIA-LDPE-2203F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® 2203F is a low density polyethylene grade, produced by high pressure autoclave technology, suitable for blown or cast film applications. This material offers easy processability and good balance of mechanical properties. TYPICAL APPLICATIONS
-Construction and agricultural films Recommended melt temperature range from 170 to 220°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.60 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 23.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 400 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 450 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm, blown film | 5.0 | N | ISO 6383-2 |
| TD : 40 µm, blown film | 6.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A |
| Additional Information |
|---|
| Data taken from 40 µm thickness film, blow up ratio 2.5:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TATREN® IM 100 85 | Slovnaft Petrochemicals, s.r.o. | PP Impact Copolymer | TATREN® |
| Toraypef® 30050 AE20 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| Iupilon® GSH2020SR 9920A | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LNP™ LUBRICOMP™ WL0049 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |
| Sylvin 9785-79 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |