KOPA® KN133HB30HIBL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | seHn9C_KOPA-KN133HB30HIBL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPA® KN133HB30HIBL is a Polyamide 6 (Nylon 6) product. It is available in Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 to 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.40 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 107 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 5390 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 147 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, Unannealed | 190 | °C | |
| 1.8 MPa, Unannealed | 180 | °C | |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.50 | ASTM D150 | |
| Arc Resistance | 130 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 5503N-PE | TSRC Corporation | TPE | T-Blend® |
| THERMORUN® 5850N | Mitsubishi Chemical Performance Polymers, Inc. | TPE | THERMORUN® |
| Capilene® HT 75 A | Carmel Olefins Ltd. | PP Impact Copolymer | Capilene® |
| Latamid 66 H2 G/35-V0KB3 | LATI S.p.A. | Nylon 66 | Latamid |
| OmniTech™ PMA IM UV | OMNI Plastics, LLC | Acrylic (PMMA) | OmniTech™ |