Daplen™ EG250AI
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Daplen™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sduChG_Daplen-EG250AI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daplen EG250AI is a 20% mineral reinforced impact modified polypropylene compound suitable for injection moulding. This material has an excellent balance between impact strength and stiffness, gives a good surface quality and is easy to process. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Shrinkage 1 | Internal method | ||
| Anisotropic | 0.10 | % | Internal method |
| Isotropic | 0.70 | % | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Atomization- 16 hr (100°C) | mg | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | 50.0 | µgC/g | VDA 277 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 35.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1.75 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 21.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.2 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 1.80 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.5 | kJ/m² | ISO 179/1eA |
| 23°C | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 70 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 93.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 52.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 126 | °C | ISO 306/A |
| -- | 49.0 | °C | ISO 306/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 3.00 - 6.00 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 to 80°CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 to 200 m/min |
| Note Message | |
|---|---|
| 1 . | Radial Disk |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Roechling SUSTAPEI | Röchling Sustaplast SE & Co. KG | PEI | Roechling |
| Precision Polymer A75H | Precision Polymer Engineering Ltd. | Rubber | Precision Polymer |
| Sindustris PC EC5001AF | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Iupiace® GX1210 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| LEXAN™ HPH4504H resin | SABIC Innovative Plastics | PPC | LEXAN™ |