Order Products : sales@su-jiao.com
LNP™ LUBRICOMP™ VN001 compound
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sd9Q89_LNP-LUBRICOMP-VN001-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP VN001 is a compound based on Super Tough Nylon containing 2% MOS2. Added feature of th is grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound VL-4210 D Product reorder name: VN001 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 5.0 | % | |
| Across Flow : 24 hr | 2.0 to 5.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.80 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2290 | MPa | ASTM D638 |
| -- | 2390 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 53.9 | MPa | ASTM D638 |
| Yield | 56.4 | MPa | ISO 527-2/5 |
| Break 3 | 48.3 | MPa | ASTM D638 |
| Break | 53.8 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 38 | % | ASTM D638 |
| Yield | 5.3 | % | ISO 527-2/5 |
| Break 5 | 41 | % | ASTM D638 |
| Break | 28 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1910 | MPa | ASTM D790 |
| -- 7 | 2080 | MPa | ISO 178 |
| Flexural Stress | 69.6 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.79 | ||
| vs. Itself - Static | 0.36 | ||
| Flexural Strain at Break 8 | 4.0 | % | ISO 178 |
| Wear Factor - Washer | 71.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 160 | J/m | ASTM D256 |
| 23°C 9 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1700 | J/m | ASTM D4812 |
| 23°C 10 | 180 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 22.3 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 216 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 210 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 64.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.2E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.2E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 260 to 271 | °C | |
| Middle Temperature | 277 to 288 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 293 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP640V | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| AIE PA6 50G3F | Asia International Enterprise (Hong Kong) Limited | Nylon 6 | AIE PA6 |
| LNP™ STAT-KON™ EE003XXC compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |
| Plaslube® PA6 GL10 | Techmer Engineered Solutions | Nylon 6 | Plaslube® |
| Sylvin 4260-50 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |