Generic PPS - Glass Fiber
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sd28gQ_Generic-PPS---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPS - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.57 - 1.68 | g/cm³ | ASTM D792 |
| 23°C | 1.51 - 1.72 | g/cm³ | ISO 1183 |
| -- | 1.50 - 1.78 | g/cm³ | ASTM D1505 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.10 - 0.40 | % | ASTM D955 |
| Transverse flow : 23°C | 0.30 - 1.2 | % | ASTM D955 |
| 23°C | 0.18 - 0.81 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.010 - 0.025 | % | ASTM D570 |
| 23°C, 24 hr | 0.020 - 0.041 | % | ISO 62 |
| Saturated, 23°C | 0.020 | % | ISO 62 |
| Equilibrium, 23°C | 0.020 - 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 100 - 124 | ASTM D785 | |
| 23°C | 100 - 122 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 8780 - 18100 | MPa | ASTM D638 |
| 23°C | 11900 - 15300 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 91.5 - 200 | MPa | ASTM D638 |
| Yield, 23°C | 107 - 202 | MPa | ISO 527-2 |
| Fracture, 23°C | 85.2 - 200 | MPa | ASTM D638 |
| Fracture, 23°C | 117 - 195 | MPa | ISO 527-2 |
| 23°C | 83.9 - 192 | MPa | ASTM D638 |
| 23°C | 144 - 201 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 0.95 - 1.6 | % | ASTM D638 |
| Fracture, 23°C | 0.98 - 2.0 | % | ASTM D638 |
| Fracture, 23°C | 0.94 - 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 6090 - 18000 | MPa | ASTM D790 |
| 23°C | 12000 - 14800 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 85.2 - 280 | MPa | ASTM D790 |
| 23°C | 187 - 292 | MPa | ISO 178 |
| Yield, 23°C | 149 - 160 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 128 - 278 | MPa | ASTM D695 |
| Shear Strength (23°C) | 74.5 - 80.0 | MPa | ASTM D732 |
| Poisson's Ratio (23°C) | 0.36 - 0.40 | ASTM E132 | |
| Coefficient of Friction | 0.33 - 0.35 | ASTM D1894 | |
| Taber Abrasion Resistance (23°C) | 49.9 - 50.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 - 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 8.7 - 56 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 51 - 100 | J/m | ASTM D256 |
| 23°C | 4.5 - 14 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 91 - 690 | J/m | ASTM D256 |
| 23°C | 15 - 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 259 - 266 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 275 - 280 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 259 - 268 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 260 - 273 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 115 - 215 | °C | ISO 75-2/C |
| Melting Temperature | |||
| -- | 280 - 285 | °C | |
| -- | 278 - 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| Flow | 6.0E-6 - 2.7E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.4E-5 - 2.1E-5 | cm/cm/°C | ASTM E831 |
| Flow | 6.0E-6 - 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.1E-5 - 2.4E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 4.0E-5 - 9.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 4.0E-5 - 5.1E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.25 - 0.39 | W/m/K | ASTM C177 |
| UL Temperature Rating | 209 - 210 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 55 - 1.3E+16 | ohms | ASTM D257 |
| -- | 1.0E+4 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 10 - 1.1E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+15 - 2.6E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 14 - 22 | kV/mm | ASTM D149 |
| 23°C | 13 - 28 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.50 - 5.00 | ASTM D150 | |
| 23°C | 3.90 - 4.60 | IEC 60250 | |
| 23°C | 3.91 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 9.9E-4 - 2.1E-3 | ASTM D150 | |
| 23°C | 1.0E-3 - 2.4E-3 | IEC 60250 | |
| Arc Resistance | 117 - 127 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 130 - 190 | V | UL 746 |
| Comparative Tracking Index | |||
| -- | 121 - 225 | V | IEC 60112 |
| -- | 168 - 170 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 44 - 57 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 - 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 280 - 323 | °C | |
| Middle Temperature | 304 - 330 | °C | |
| Front Temperature | 305 - 336 | °C | |
| Nozzle Temperature | 295 - 330 | °C | |
| Processing (Melt) Temp | 317 - 335 | °C | |
| Mold Temperature | 135 - 158 | °C | |
| Injection Pressure | 73.5 - 87.4 | MPa | |
| Holding Pressure | 45.0 - 50.5 | MPa | |
| Back Pressure | 0.258 - 1.54 | MPa | |
| Screw Speed | 45 - 101 | rpm | |
| Clamp Tonnage | 4.5 - 9.0 | kN/cm² | |
| Cushion | 4.50 - 9.53 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPS - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ MAXBATCH YM-618.G001-1000 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| POLYLON IR 1700 | POLYMA Kunststoff GmbH & Co. KG | PC | POLYLON |
| Xuchuan XCW-35N | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| IDI BMC B10 (Glass Content 10%) | IDI Composites International | TS, Unspecified | IDI BMC |
| Sylvin 4200-88 White 1523 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |