LNP™ LUBRICOMP™ QL004 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | scLGeq_LNP-LUBRICOMP-QL004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP QL004 is a compound based on Nylon 6/10 containing 20% PTFE. Added features of this grade include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound QL-4040 Product reorder name: QL004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.26 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.37 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2430 | MPa | ASTM D638 |
| -- | 2490 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 53.0 | MPa | ASTM D638 |
| Yield | 53.0 | MPa | ISO 527-2/5 |
| Break 3 | 53.0 | MPa | ASTM D638 |
| Break | 52.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 14 | % | ASTM D638 |
| Yield | 11 | % | ISO 527-2/5 |
| Break 5 | 16 | % | ASTM D638 |
| Break | 11 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1710 | MPa | ASTM D790 |
| -- 7 | 2320 | MPa | ISO 178 |
| Flexural Stress | 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 39 | J/m | ASTM D256 |
| 23°C 8 | 4.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 680 | J/m | ASTM D4812 |
| 23°C 9 | 32 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 3.20 | J | ASTM D3763 |
| -- | 1.40 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 181 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 170 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 56.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 60.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.1E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANBLEND FS7 FR UV | Polykemi AB | ASA+PC | SCANBLEND |
| Unichem 9066G-015 | Colorite Polymers | PVC, Unspecified | Unichem |
| ACCUTECH™ CP0437T30L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Chemlon® 217 GI | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| LNP™ STAT-KON™ PX08019 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ STAT-KON™ |