Order Products : sales@su-jiao.com
Propafilm™ RD85
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sc0UkC_Propafilm-RD85.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Differentially Barrier Coated Film Biaxially oriented polypropylene (BOPP) film coated on one side with an aqueous dispersion of polyvinylidene chloride (PVdC) copolymer, the other side coated with an aqueous acrylic dispersion. RD85/100 are suitable for use as a single film or in laminates for overwrapping and form-fill-seal packaging especially in the bakery and confectionery industries. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 121°C, 1 min | 4.0 | % | |
| Flow : 129°C, 1 min | 7.0 | % | |
| Across Flow : 129°C, 1 min | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.25 | ||
| vs. Itself - Static, Outside/Outside | 0.25 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 2200 | µm | |
| Seal Strength | Internal Method | ||
| -- 1 | 0.15 | N/mm | |
| -- 2 | 0.15 | N/mm | |
| Seal Initiation Temperature | Internal Method | ||
| -- 3 | 104 to 146 | °C | |
| -- 4 | 85.0 to 146 | °C | |
| Oxygen Permeability (25°C, 0% RH) | 0.74 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 5.4 | g/m²/24 hr | ASTM F1770 |
| Yield | 51.0 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 100 | ASTM D2457 | |
| Haze 5 | 2.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | PVdC/PVdC; 265°F; 2secs; 15psi |
| 2 . | Acrylic/Acrylic; 265°F; 2secs; 15psi |
| 3 . | PVdC/PVdC; 2secs; 15psi |
| 4 . | Acrylic/Acrylic; 2secs; 15psi |
| 5 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| GAPEX® RPP06EB94NA | Ferro Corporation | PP, Unspecified | GAPEX® |
| KOPA® KN333HB38BL | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| LEXAN™ ML7686 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Pinnacle PP 4150H | Pinnacle Polymers | PP Impact Copolymer | Pinnacle PP |
| OTECH ALLOY NT7000-90 - Profile | OTECH Corporation | TP, Unspecified | OTECH ALLOY |