ASTALON™ GS2010R
| Category: | PC , Polycarbonate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | saenDZ_ASTALON-GS2010R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTALON™ GS2010R is a 10% glass fibre filled Polycarbonate and offers an exceptional combination of product rigidity and strength, heat resistance, dimensional stability, flame retardancy, creep resistance and processability with a mould release agent (R) to assist with moulded part ejection. Typical applications of ASTALON™ GS2010R include metal substitution such as automotive interior structural brackets, camera frames, industrial electrical switch housings, electrical power tool casings and mounting chassis for electronics devices such as computer printers, laptop computers and VTR units. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.14 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 124 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 71.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 7.0 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 3650 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 116 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 143 | °C | ASTM D648 |
| CLTE - Flow | 4.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.88 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 125 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 275 to 295 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 110 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GA-3133S-CCUV | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Wire & Cable |
| RheTech Polypropylene G40P100-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Baydur® 726 IBS (40 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Chemlon® 133 GH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Sylvin 8999-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |