Generic Nylon 12 - Carbon Fiber
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sZ4mkG_Generic-Nylon-12---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 12 - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 - 1.30 | g/cm³ | ASTM D792 |
| 23°C | 1.06 - 1.15 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.050 - 0.20 | % | ASTM D955 |
| 23°C | 0.20 - 0.51 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 4140 - 21400 | MPa | ASTM D638 |
| 23°C | 8380 - 16200 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 110 - 165 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 2.5 - 3.8 | % | ASTM D638 |
| Fracture, 23°C | 1.0 - 4.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 6100 - 14000 | MPa | ASTM D790 |
| 23°C | 6830 - 7250 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 117 - 241 | MPa | ASTM D790 |
| 23°C | 90.0 - 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 52 - 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 480 - 1100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 163 - 177 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 160 - 165 | °C | ISO 75-2/A |
| Continuous Use Temperature | 90.0 - 150 | °C | ASTM D794 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 105 | °C | |
| Drying Time | 3.9 - 8.0 | hr | |
| Rear Temperature | 221 - 241 | °C | |
| Middle Temperature | 227 - 250 | °C | |
| Front Temperature | 232 - 261 | °C | |
| Processing (Melt) Temp | 231 - 251 | °C | |
| Mold Temperature | 76.6 - 90.0 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 12 - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SGH4340D | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| TEKNIFLEX® VPOA10300 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/EVOH/PE/PCTFE | TEKNIFLEX® |
| BMC T15(GP) | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| CMET TSR-829 | CMET Inc. | Epoxy | CMET |
| Osterlene® HB0554 | Osterman & Company | HDPE | Osterlene® |