SCHULAMID® 66 MV 5 FR Datasheet,Nylon 66,A. Schulman Europe-SHANGHAI SUSHENG

Message
Medium viscosity flame-retardant Polyamide 66 grade, V-0 by 0,38 mm; halogen free

General Information
Features	Low smoke Halogen-free No antimony Flame retardancy
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.14	g/cm³	ISO 1183/A
Viscosity Number	152	cm³/g	ISO 307

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3600	MPa	ISO 527-2/1A/1
Tensile Stress (Yield)	80.0	MPa	ISO 527-2/1A/50
Tensile Strain (Yield)	4.9	%	ISO 527-2/1A/50
Flexural Modulus ¹	3700	MPa	ISO 178
Flexural Stress			ISO 178
6.3% strain	130	MPa	ISO 178
3.5% strain ²	115	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	5.0	kJ/m²	ISO 179/1eA
23°C	3.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	25	kJ/m²	ISO 179/1eU
23°C	70	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	222	°C	ISO 75-2/Bf
Vicat Softening Temperature	240	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flammability Classification			IEC 60695-11-10, -20
0.380 mm	V-0		IEC 60695-11-10, -20
0.800 mm	V-0		IEC 60695-11-10, -20
1.50 mm	V-0		IEC 60695-11-10, -20
3.00 mm	V-0		IEC 60695-11-10, -20
Glow Wire Flammability Index			IEC 60695-2-12
0.750 mm	960	°C	IEC 60695-2-12
1.50 mm	960	°C	IEC 60695-2-12
3.00 mm	960	°C	IEC 60695-2-12
Oxygen Index	35	%	ISO 4589-2

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	3.0 - 4.0	hr
Suggested Max Moisture	0.040 - 0.10	%
Hopper Temperature	80.0	°C
Rear Temperature	250	°C
Middle Temperature	265	°C
Front Temperature	280	°C
Processing (Melt) Temp	280	°C
Mold Temperature	60.0 - 100	°C
Injection Pressure	80.0 - 140	MPa
Holding Pressure	40.0 - 85.0	MPa
Back Pressure	2.00 - 8.00	MPa
Screw Speed	250	mm/sec

Injection instructions
Characteristic propertiesSCHULAMID ... FR is the trade name of the halogen and (red) phosphorous free flame retardant Polyamide 6, 66 and 66/6 grades.Predrying"Typically a minimum predrying time of 3 to 4 hours at 80°C is recommended inan dehumidifying dryer. For optimal qualities a humidity of 0,04 - 0,1 % isrecommended.. Drying over 6 hours duration should occur at 60°C.should be placed in the hopper"ReprocessingAddition of regrind is not recommended for nylons containing flame retardant.Shut down"Long residence time should be avoided. Purge with polyolefin or with basepolymer."Finishing"The material is suitable for machining. Varnishing, printing, gluing andembossing can be carried out using commercially available products."Conditioning"Recently processed mouldings which not have been conditioned are brittle. Thematerial picks up moisture until the equilibrium moisture content is reached.This may last for over a half year. Then the article has reached his balancedproperty profile. For accelerated absoption see our separate Technicalinstruction."Remarks"For permanent processing of glass fibre reinforced grades wear resistant screwsand cylinders are recommended."

Injection instructions

Characteristic propertiesSCHULAMID ... FR is the trade name of the halogen and (red) phosphorous free flame retardant Polyamide 6, 66 and 66/6 grades.Predrying"Typically a minimum predrying time of 3 to 4 hours at 80°C is recommended inan dehumidifying dryer. For optimal qualities a humidity of 0,04 - 0,1 % isrecommended.. Drying over 6 hours duration should occur at 60°C.should be placed in the hopper"ReprocessingAddition of regrind is not recommended for nylons containing flame retardant.Shut down"Long residence time should be avoided. Purge with polyolefin or with basepolymer."Finishing"The material is suitable for machining. Varnishing, printing, gluing andembossing can be carried out using commercially available products."Conditioning"Recently processed mouldings which not have been conditioned are brittle. Thematerial picks up moisture until the equilibrium moisture content is reached.This may last for over a half year. Then the article has reached his balancedproperty profile. For accelerated absoption see our separate Technicalinstruction."Remarks"For permanent processing of glass fibre reinforced grades wear resistant screwsand cylinders are recommended."

Note Message
1 .	2.0 mm/min
2 .	2.0 mm/min

Category:	Nylon 66 , Polyamide 66
Manufacturer:	A. Schulman Europe
Trademark:	SCHULAMID®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	sZ0zAb_SCHULAMID-66-MV-5-FR.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SLOVALEN® PC 51 T 25	Plastcom	PP, Unspecified	SLOVALEN®
BP PPC 0510 BLK	Buckeye Polymers, Inc.	PP Copolymer	BP
Hanwha Total PP TI54	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, High Crystal	Hanwha Total PP
Karina BLACK PVC COMPOUND 751-48/ 1-BYR-IS (*)	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LGE 355SE	LG Polymers India Pvt. Ltd.	PS (EPS)	LGE