ACCUTECH™ HP0339G10M20CL
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sYEPgE_ACCUTECH-HP0339G10M20CL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0339G10M20CL is a polypropylene homopolymer (PP Homopoly) product, which contains 10% glass fiber reinforced materials and 20% mineral fillers. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 81 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3600 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 41.0 | MPa | ASTM D638 |
| Fracture | 40.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | ASTM D638 |
| Fracture | 6.0 | % | ASTM D638 |
| Flexural Modulus | 4000 | MPa | ASTM D790 |
| Flexural Strength | 64.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 151 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 109 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 30% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 6208-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Celcon® CF802 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| LNP™ THERMOCOMP™ RF008XXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Capilene® CT 71 A | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |
| Sylvin 8250-90 White 1570 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |