FRIANYL® B3 M10 V2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nilit Plastics |
| Trademark: | FRIANYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sWQtIc_FRIANYL-B3-M10-V2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FRIANYL® B3 M10 V2 is a Polyamide 6 (Nylon 6) compound, 10% mineral filled, flame retardant, halogen and red phosphorous free, UL listed V2. This compound is intended for injection molding. FRIANYL® B3 M10 V2 is primarily designed for the Electrical and Electronic industry. It is also suitable for Automotive applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.25 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 1.3 | % | |
| Flow : 23°C | 0.70 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.5 | % | |
| Saturation, 23°C | 6.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3600 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 3.5 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 190 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 105 | °C | IEC 60216 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 21 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 550 | V | IEC 60112 |
| Needle Flame Test | IEC 60695-11-5 | ||
| 1.00 mm | Pass | ||
| 2.00 mm | Pass |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 960 | °C | |
| 3.20 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 750 | °C | |
| 3.20 mm | 775 | °C |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| 2 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom EP6140 B1 | Spartech Polycom | PP, Unspecified | Spartech |
| ACCUTECH™ HP0334G10CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Bapolene® LD100F | Bamberger Polymers, Inc. | LDPE | Bapolene® |
| Karina BLACK PVC COMPOUND 771-48/ 1-BY-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OnForce™ LFT 5200-5001 FR Natural | PolyOne Corporation | Polyolefin, Unspecified | OnForce™ LFT |