Bayblend® W85 HI
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Bayblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sWCRl9_Bayblend-W85-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+ASA) blend; improved weather resistance; optimized heat ageing stability; excellent low temperature ductility; high heat resistance; Vicat/B 120 = 134 °C. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 17.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 56.0 | MPa | |
| Break, 23°C | 58.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 5.0 | % | |
| Break, 23°C | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 38 | kJ/m² | |
| 23°C | 48 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 45.0 | J | |
| 23°C | 45.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 134 | °C | ISO 306/B120 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 1(260°C) | 275 | Pa·s | ISO 11443-A |
| Note Message | |
|---|---|
| 1 . | 1000/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer PBT-11020-GFFR | Polylink Polymers (India) Ltd. | PBT | Polylink Polymer |
| RTP 299 M X 131268 G | RTP Company | Nylon 1010 | RTP |
| Verolloy D200 | PlastxWorld Inc. | PC Alloy | Verolloy |
| Generic COC | Generic | COC | Generic |
| Lupoy® GP5001AF | LG Chem Ltd. | PC+ABS | Lupoy® |