EMERGE™ PC/ABS 7530
| Category: | PC+ABS , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sVW1d3_EMERGE-PC-ABS-7530.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC/ABS 7530 advanced resin is a high flow, ignition-resistant PC/ABS blend that contains no chlorine or bromine flame retardants. It has good property balance of flow ability, impact and heat stability. It is suitable for the injection molding for large, thin-wall and Intricate parts. It can be used in a wide variety of applications in the Information Technology Equipment and Consumer Electronics Industries Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/3.8 kg | 16 | g/10 min | |
| 260°C/5.0 kg | 70 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 62.1 | MPa | |
| Break, 3.20 mm, Injection Molded | 45.5 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 4.0 | % | |
| Break, 3.20 mm, Injection Molded | 60 | % | |
| Flexural Modulus (3.20 mm, Injection Molded) | 2830 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 97.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 95.0 | °C | |
| 1.8 MPa, Unannealed | 82.8 | °C | |
| Vicat Softening Temperature | 108 | °C | ASTM D1525 1 |
| Ball Indentation Temperature | 90.0 | °C | IEC 60335-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 2(1.50 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index 3(2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature 4(2.00 mm) | 925 | °C | IEC 60695-2-13 |
| Oxygen Index 5 | 29 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 to 90.6 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 60.0 to 90.6 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4183 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TRIBIT® 1800H | Samyang Corporation | PBT | TRIBIT® |
| ChronoFlex® C 75D | CardioTech International, Inc. | PUR, Unspecified | ChronoFlex® |
| EPO-TEK® H20E-175 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LNP™ STAT-KON™ DX05301C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |