Salflex 620KC4
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Salflex Polymers Ltd. |
| Trademark: | Salflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sV9Tc7_Salflex-620KC4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Salflex 620KC4 is a polypropylene product that contains 20% calcium carbonate filler. It can be processed by blow molding or extrusion and is available in North America. The application fields of Salflex 620KC4 include electrical appliances and automobile industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.1 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 60 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 17.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 500 | % | ISO 527-2 |
| Flexural Modulus | 1110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 65 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Additional Information |
|---|
| Ash Content, ISO 3451/1A: 19%Tensile Strain at Break, ISO 527: >500% |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 190 - 225 | °C | |
| Cylinder Zone 2 Temp. | 190 - 230 | °C | |
| Cylinder Zone 3 Temp. | 190 - 235 | °C | |
| Cylinder Zone 4 Temp. | 190 - 235 | °C | |
| Melt Temperature | 200 - 240 | °C | |
| Die Temperature | 190 - 235 | °C |
| Extrusion instructions |
|---|
| Blow Molding Mold Temperature: 50 to 85°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hanwha Total PP BI750 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| HOPELEX PC-1070S | Lotte Chemical Corporation | PC | HOPELEX |
| PlexTuf 2000 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | PlexTuf |
| POLIMAXX KU650 | IRPC Public Company Limited | ABS | POLIMAXX |
| LEXAN™ EXL1182T resin | SABIC Innovative Plastics | PC | LEXAN™ |