Chemlon® MDS2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sU8qbI_Chemlon-MDS2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MDS2 is a 50% glass sphere filled nylon 6 that offers excellent rigidity coupled with minimal distortion. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.50 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 1.0 - 1.5 | -- | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.80 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5200 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 65.0 | 38.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 5000 | 2000 | MPa | ISO 178 |
| Flexural Stress 2 | 120 | 50.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | 20 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 35 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | > 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 130 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 10 | 9.0 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.80 | 4.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.080 | IEC 60250 | |
| Comparative Tracking Index | 525 | 500 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Oxygen Index | 22 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 - 280 | °C | |
| Middle Temperature | 230 - 280 | °C | |
| Front Temperature | 230 - 280 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 200 | rpm |
| Injection instructions |
|---|
| Back pressure: LowInjection pressure: HighThe material is supplied dry and ready to mould in sealed, moisture proof sacks. No drying is necessary unless the materials has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present. Should drying become necessary two hours at 80 - 100°C in a vacuum oven is recommended. Alternatively material maybe dried for up to six hours in a hopper drier or an air circulating oven at a temperature not exceeding 80°C. |
| Note Message | |
|---|---|
| 1 . | Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| 2 . | Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD 2582 | RTP Company | PC+ABS | RTP |
| Crastin® HR5315HF NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Generic PAEK | Generic | PAEK | Generic |
| Hypro® PP- CP 35/1.5C | Entec Polymers | PP Impact Copolymer | Hypro® |
| Sylvin 7833-75 Red 6285 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |