Grilon® TSS/4 LF 2
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sTzZwI_Grilon-TSS-4-LF-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grilon® TSS/4 LF 2 is a Polyamide 66/6 Copolymer (Nylon 66/6) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Grilon® TSS/4 LF 2 are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.16 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.90 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 140 | 65.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3300 | 1400 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield | 90.0 | 50.0 | MPa | |
| Break | 70.0 | -- | MPa | |
| Tensile Strain (Yield) | 5.0 | 15 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 12 | > 50 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | 4.0 | kJ/m² | |
| 23°C | 4.0 | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 85.0 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/C |
| Continuous Use Temperature | Internal Method | |||
| -- 1 | 80.0 to 100 | -- | °C | |
| -- 2 | 200 | -- | °C | |
| Melting Temperature 3 | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 8.0E-5 | -- | cm/cm/°C | |
| Transverse | 9.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 27 | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 475 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA66+PA6, MHRS, 14-030N, Z2 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | Long Term |
| 2 . | Short Term |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® CP 1002 | Plastic Solutions, Inc. | PP Impact Copolymer | PrimaFlex® |
| Veroplas SKG30 | PlastxWorld Inc. | ABS | Veroplas |
| Wellamid® 22LHI6 XE-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Europrene® 1739 | Versalis S.p.A. | SBR, Emulsion | Europrene® |
| ISOTHANE® 1680A-EL | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyether | ISOTHANE® |