Order Products : sales@su-jiao.com
Riblene® FF 34
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sSvw84_Riblene-FF-34.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene FF 34 is a high molecular weight low density polyethylene (LDPE), additivated with slip and antiblocking agent, suitable for blown film extrusion. Riblene FF 34 is characterised by a good melt strength leading to a good bubble stability during extrusion Films manufactured by Riblene FF 34 are easily heat shrinkable and characterised by good mechanical properties. Main Application Riblene FF 34 is recommended for the production of general packaging film, shoppers, lamination film and blend. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.15 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 70 | µm | |
| Film Thickness - Recommended / Available | 30 to 120 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 70 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD : 70 µm, Blown Film | 190 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 70 µm, Blown Film | 10.0 | MPa | |
| TD : Yield, 70 µm, Blown Film | 11.0 | MPa | |
| MD : Break, 70 µm, Blown Film | 22.0 | MPa | |
| TD : Break, 70 µm, Blown Film | 19.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 70 µm, Blown Film | 400 | % | |
| TD : Break, 70 µm, Blown Film | 600 | % | |
| Dart Drop Impact 1(70 µm, Blown Film) | 180 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 70.0 µm | 45.0 | kN/m | |
| TD : 70.0 µm | 60.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
| Melting Temperature | 113 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 70.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (70.0 µm, Blown Film) | 9.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Royalite R60 | Spartech Plastics | PMMA+PVC | Royalite |
| Shandong PA1212 A4S11 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| COPYLENE® CR350LN | Phillips 66 | PP Random Copolymer | COPYLENE® |
| Daelim Po1y® HX-102F | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Pharmalene® FL 20 PH | Versalis S.p.A. | LDPE | Pharmalene® |