DOW™ HDPE KT 10000 UE
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sSQcI5_DOW-HDPE-KT-10000-UE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HDPE KT 10000 UE Polyethylene Resin is an UV stabilised resin with very narrow molecular weight distribution. It was developed to impart excellent stiffness, combined with good impact strength to injection moulded parts, at minimum warpage. Note: HDPE KT 10000 UE Polyethylene Resin should comply with FDA regulation 177.1520 and with most European food contact regulations when used unmodified and processed according to good manufacturing practices for food contact applications. Please, contact your nearest Dow office for food contact compliance statements. The purchaser remains responsible for determining whether the use complies with all relevant regulations. Applications:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.964 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 8.0 | g/10 min | |
| 190°C/5.0 kg | 22 | g/10 min | |
| Spiral Flow | 73.5 | cm | Internal Method |
| Molding Shrinkage - Flow | 2.1 | % | ASTM D955 |
| Environmental Stress-Cracking Resistance (100% Antarox CO-630, Compression Molded) | 2.50 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 29.0 | MPa | |
| Break, Compression Molded | 32.0 | MPa | |
| Tensile Elongation (Break, Compression Molded) | 800 | % | ASTM D638 |
| Flexural Modulus - 2% Secant (Compression Molded) | 1050 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength (Compression Molded) | 77.0 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 131 | °C | ISO 306/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ MD 4245-59770 | PolyOne Corporation | PP Copolymer | Maxxam™ |
| Telcar® SGI50050 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Zhongfa PP FR-28 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Later 4 G/50 | LATI S.p.A. | PBT | Later |
| PLUSTEK RB301G6 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |