NORYL™ NHP9023 resin
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sSLM3S_NORYLNHP9023resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NORYL NHP9023 resin is 15% glass fiber reinforced, with a non-halogen flame retardant (UL94 V-0 at 1.5 mm) and high heat distortion temperature (150 C) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.20 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5400 | MPa | ASTM D638 |
| -- | 5600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 112 | MPa | ASTM D638 |
| Fracture | 112 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 2.9 | % | ASTM D638 |
| Fracture | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 5200 | MPa | ASTM D790 |
| -- 5 | 5200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 163 | MPa | ISO 178 |
| Yield, 50.0mm span 6 | 163 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 61 | J/m | ASTM D256 |
| 23°C | 72 | J/m | ASTM D256 |
| -30°C 8 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 9 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 500 | J/m | ASTM D4812 |
| 23°C | 500 | J/m | ASTM D4812 |
| -30°C 10 | 28 | kJ/m² | ISO 180/1U |
| 23°C 11 | 27 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 10.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 153 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 154 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 155 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 161 | °C | ISO 306/B50 |
| -- | 163 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : 23 to 80°C | 3.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : 23 to 80°C | 6.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.75 mm | V-1 | UL 94 | |
| 1.5 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 266 - 316 | °C | |
| Middle Temperature | 277 - 321 | °C | |
| Front Temperature | 288 - 327 | °C | |
| Nozzle Temperature | 299 - 327 | °C | |
| Processing (Melt) Temp | 299 - 327 | °C | |
| Mold Temperature | 82 - 110 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME GPPS SC206E | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| LOXIM 130 01 HB | LOXIM Industries Private Limited | PC | LOXIM |
| OMIKRON BG 902 NERO | TECNOPOL | PP Homopolymer | OMIKRON |
| Hostacom X M2 T24 G71260 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| TECHNYL STAR® S 60G1 V30 GREY R7011 | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |