LNP™ LUBRICOMP™ ZX05506 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sSG49X_LNP-LUBRICOMP-ZX05506-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* ZX05506 is a compound based on PPE+PS Blend resin containing 15% Graphite Powder, 20% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound ZML-4334 Product reorder name: ZX05506 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.54 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4900 | MPa | ASTM D638 |
| -- | 4910 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 52.5 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.4 | % | ASTM D638 |
| Break | 2.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4960 | MPa | ASTM D790 |
| -- | 5370 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 99.2 | MPa | ASTM D790 |
| -- | 94.7 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.34 | ||
| vs. Itself - Static | 0.34 | ||
| Wear Factor - Washer | 174 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 32 | J/m | ASTM D256 |
| 23°C 2 | 2.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 180 | J/m | ASTM D4812 |
| 23°C 3 | 13 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.80 | J | ASTM D3763 |
| -- | 1.23 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 122 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 126 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 to 288 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 299 to 310 | °C | |
| Processing (Melt) Temp | 299 to 304 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 AR 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| Vital-Line SHM3300G | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| NEOFLON™ AC-5500 | DAIKIN AMERICA, INC. | PFA | NEOFLON™ |
| Hypro® PPC-GF10 NATURAL | Entec Polymers | PP Impact Copolymer | Hypro® |
| Karina IVORY PVC COMPOUND -E 858-35/ 1-DY-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |