HiFill® PA6 IM 511 HS L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sSCg1s_HiFill-PA6-IM-511-HS-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PA6 IM 511 HS L is a Polyamide 6 (Nylon 6) product. It can be processed by injection molding and is available in North America. Typical application: Low Temperature Applications. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.90 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.5 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 70 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 150 | % | ASTM D638 |
| Flexural Modulus | 1590 | MPa | ASTM D790 |
| Flexural Strength | 58.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | No Break | ||
| 23°C, 3.18 mm | No Break | ||
| Unnotched Izod Impact (3.18 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 166 | °C | |
| 1.8 MPa, Unannealed | 71.1 | °C | |
| CLTE - Flow | 2.7E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 17 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 254 to 291 | °C | |
| Middle Temperature | 254 to 291 | °C | |
| Front Temperature | 254 to 291 | °C | |
| Processing (Melt) Temp | 238 to 277 | °C | |
| Mold Temperature | 65.6 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Geon™ Vinyl Rigid Extrusion L1361 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| KRALASTIC® KU-670 R-2 | Nippon A&L Inc. | ABS | KRALASTIC® |
| Hostacom CR 1171 G3 | LyondellBasell Industries | PP Impact Copolymer | Hostacom |
| Petrotene® PP A3 G45 NTLA010 PH367 | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |
| Pinnacle PP 1508 | Pinnacle Polymers | PP Homopolymer | Pinnacle PP |