Lumid® HM2604A(W)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sQvIKs_Lumid-HM2604A-W-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lumid® HM2604A(W) is a Polyamide 6 (Nylon 6) material filled with 60% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Lumid® HM2604A(W): High Stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C, 3.20 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 130 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 206 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 15700 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 304 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 205 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 3.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 3.50 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 290 | °C | |
| Front Temperature | 260 to 290 | °C | |
| Nozzle Temperature | 260 to 290 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC/TP-GP3-G30 | Polymer Resources Ltd. | PC+Polyester | PRL |
| Sanren EVA 14/15 | SINOPEC Shanghai Petrochemical Co. Ltd. | EVA | Sanren |
| Durethan® BC 30 S 000000 | LANXESS GmbH | Nylon 6 | Durethan® |