Somos® NeXt LV Grey
| Category: | Unspecified , Unspecified |
| Manufacturer: | DSM Somos® |
| Trademark: | Somos® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sNrOlY_Somos-NeXt-LV-Grey.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Somos® NeXt LV Grey creates tough, ABS-like parts with a high modulus while maintaining a low viscosity for effortless cleaning. Somos® NeXt LV Grey has good water resistance and thermal properties. This third generation Somos® high impact material focuses on creating quality resins that can produce tough, complex parts. Applications Somos® NeXt LV Grey produces parts that are more resistant to fracture and cracking than standard SL resins. It is ideal for use in functional testing and low-volume manufacturing applications. This resin is excellent for functional end-use performance parts, especially snap-fit designs, impellers, connectors, and sporting goods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | |
| Water Absorption (Equilibrium) | 0.36 to 0.40 | % | ASTM D570 |
| Viscosity (30°C) | 480 | mPa·s |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Critical Exposure | 14.6 | mJ/cm² | |
| Penetration Depth | 131.1 | µm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 84 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2970 to 3290 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 60.0 to 66.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | |
| Break | 4.6 to 7.2 | % | |
| Flexural Modulus | 1840 to 2020 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 30 to 35 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648B | ||
| 0.45 MPa, Unannealed | 53.0 to 57.0 | °C | |
| 1.8 MPa, Unannealed | 49.0 to 57.0 | °C | |
| Glass Transition Temperature | 40.0 to 48.0 | °C | ASTM E1545 |
| CLTE - Flow | ASTM E831 | ||
| -- 1 | 7.4E-5 to 8.1E-5 | cm/cm/°C | |
| -- 2 | 2.2E-4 to 2.4E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 22 to 23 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.75 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.020 | ASTM D150 |
| Note Message | |
|---|---|
| 1 . | before Tg (44°C) |
| 2 . | after Tg (44°C) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP6432 9690 | Supreme Petrochem Ltd. | PS (MIPS) | SUPREME Specialty PS |
| Sylvin 9742-73 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Topolymer® 5711-951M | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Karina BROWN PVC COMPOUND 800-36/278-A-ERB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9302-70 FU BROWN 7251 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |