TOTAL Polystyrene Impact 3441
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sNrNNZ_TOTAL-Polystyrene-Impact-3441.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polystyrene Impact 3441 is a high heat resistant polystyrene for injection molding application. It is recommended for manufacturing of articles which require good dimensional stability at elevated temperatures. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Apparent Density 1 | 0.60 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.0 | g/10 min | ASTM D1238 |
| Spiral Flow 2 | 48.0 | cm | ASTM D3123 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C, Injection Molded) | 99 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, Injection Molded) | 29.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C, Injection Molded) | 65 | % | ASTM D638 |
| Flexural Modulus (23°C, Injection Molded) | 2100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 95 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 3 |
| CLTE - Flow | 9.1E-5 | cm/cm/°C | ASTM D696 |
| Heat Distortion | 81 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Dielectric Strength | 150 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 150 - 180 | °C | |
| Middle Temperature | 170 - 210 | °C | |
| Front Temperature | 190 - 230 | °C | |
| Nozzle Temperature | 210 - 250 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 200 to 240°C |
| Note Message | |
|---|---|
| 1 . | Bulk Density: Bulk Density of all Natural grades is approximately 0.6 g/cm³ |
| 2 . | Mold temperature: 220°C |
| 3 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ PTFE Compound TF 7921 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| BorSafe™ HE3497-LS | Borealis AG | HDPE | BorSafe™ |
| Braskem PE TU3001 | Braskem | LDPE | Braskem PE |
| Karina BEIGE COLOR CONCENTRATE -E 08/26-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ ZX06323 compound | SABIC Innovative Plastics Asia Pacific | PPE+PS | LNP™ THERMOCOMP™ |