3M™ Dyneon™ PTFE Compound TF 6406
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ PTFE Compound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sNW36F_3M-Dyneon-PTFE-Compound-TF-6406.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 3.73 | g/cm³ | ASTM D4745-06 |
| Apparent Density | 1.37 | g/cm³ | ASTM D4894-07 |
| Molding Shrinkage - Flow | 1.7 | % | ASTM D4894-07 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness 1(Shore D) | 72 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break) | 16.0 | MPa | ASTM D4745-06 |
| Tensile Elongation 3(Break) | 240 | % | ASTM D4745-06 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | 55.0 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | < 365 | °C |
| Note Message | |
|---|---|
| 1 . | Measured on sintered moldings |
| 2 . | Measured on sintered moldings |
| 3 . | Measured on sintered moldings |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALENE® P 100 SGF30 ST F V-0 natural | RIA-Polymers GmbH | PP, Unspecified | RIALENE® |
| MTEGRITY™ PP Homopolymer PP200 | M. Holland Company | PP Homopolymer | MTEGRITY™ PP Homopolymer |
| Nanjing Hongrui PA6 B3010 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| NOVADURAN® 5505S | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| LNP™ COLORCOMP™ HMG94MDC compound | SABIC Innovative Plastics | ABS | LNP™ COLORCOMP™ |