Vinnolit® E 70 LF

Category:	PVC, Unspecified , Polyvinyl Chloride
Manufacturer:	Vinnolit GmbH & Co. KG
Trademark:	Vinnolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	sMsRGE_Vinnolit-E-70-LF.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PVC for paste application ® Vinnolit E 70 LF is a fine-particle, paste- making copolymer of vinyl chloride and 5 % vinyl acetate yielding low viscosity plastisols with an excellent storage stability (see diagram). Due to its vinyl acetate content, Vinnolit E 70 LF can be easily processed at lower gelling temperatures. Processing and Application: Vinnolit E 70 LF may be converted into pastes by the standard methods, by dissolver or low- speed mixer. However, undue heating of the paste during mixing should be avoided since the vinyl acetate content may cause a rise in viscosity. Pastes based on Vinnolit E 70 LF can be applied by all the usual procedures. Vinnolit E 70 LF is a low temperature gelling, low-viscosity paste grade, recommended for coating heat-sensitive base fabrics, laminating pastes, carpet backings as well as automotive underbody and seam sealants. These applications also benefit from a high filler-loading capability as well as good adhesion to textile base fabrics and automotive metal surfaces. To lower paste viscosity and increase shelf life, Vinnolit E 70 LF may be blended with homopolymer extender resins such as Vinnolit EXT / Vinnolit C 65 V. Remarkable properties are: significant lower gelling temperatures good adhesion at textiles and automotive metal sheets better mechanical properties better abrasion resistance in UBC-mastics excellent storage stability of plastisols

Message

PVC for paste application

® Vinnolit E 70 LF is a fine-particle, paste- making copolymer of vinyl chloride and 5 % vinyl acetate yielding low viscosity plastisols with an excellent storage stability (see diagram).

Due to its vinyl acetate content, Vinnolit E 70 LF can be easily processed at lower gelling temperatures.

Processing and Application:
Vinnolit E 70 LF may be converted into pastes by the standard methods, by dissolver or low- speed mixer. However, undue heating of the paste during mixing should be avoided since the vinyl acetate content may cause a rise in viscosity. Pastes based on Vinnolit E 70 LF can be applied by all the usual procedures. Vinnolit E 70 LF is a low temperature gelling, low-viscosity paste grade, recommended for coating heat-sensitive base fabrics, laminating pastes, carpet backings as well as automotive underbody and seam sealants. These applications also benefit from a high filler-loading capability as well as good adhesion to textile base fabrics and automotive metal surfaces. To lower paste viscosity and increase shelf life, Vinnolit E 70 LF may be blended with homopolymer extender resins such as Vinnolit EXT / Vinnolit C 65 V.

Remarkable properties are:

significant lower gelling temperatures

good adhesion at textiles and automotive metal sheets

better mechanical properties

better abrasion resistance in UBC-mastics

excellent storage stability of plastisols

General Information
Features	Copolymer Good Abrasion Resistance Good Adhesion Low Viscosity
Uses	Automotive Applications Carpet Backing Coating Applications Laminates Sealants
Processing Method	Plastisol

Physical	Nominal Value	Unit	Test Method
Apparent Density	0.40	g/cm³	ISO 60
K-Value	70.0		ISO 1628-2
Particle Size Distribution - sieve retention ¹	< 3.0	%
Vinyl Content - acetate	5.0	%
Volatile Matter	< 0.50	%	ISO 1269

Note Message
1 .	retained on 0.063 mm screen

Resin Grade	Manufacturer	Category	Trademark
RTP 200 TFE 20 HS	RTP Company	Nylon 66	RTP
CERTENE™ PBM-5035	Muehlstein	PP Impact Copolymer	CERTENE™
Elvax® 3134SBZ	DuPont Packaging & Industrial Polymers	EVA	Elvax®
K-Prene GLC 6060	Technovinyl Polymers India Ltd.	TPE	K-Prene
NORYL™ WCD883AU resin	SABIC Innovative Plastics Asia Pacific	PPE+TPE	NORYL™