NYCOA Polyamide 6215 HS
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sMGuFi_NYCOA-Polyamide-6215-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 6215 HS is a 15% glass fiber reinforced, impact modified, Nylon 6/12 that offers an excellent balance of stiffness and impact strength. This grade features excellent dimensional stability with low moisture absorption compared to other glass filled Nylons. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 101 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 10 | % | ASTM D638 |
| Flexural Modulus 3 | 3600 | MPa | ASTM D790 |
| Flexural Strength 4 | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 217 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 227 - 238 | °C | |
| Middle Temperature | 238 - 249 | °C | |
| Front Temperature | 243 - 260 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 243 - 260 | °C | |
| Mold Temperature | 65.6 - 76.7 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.517 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® B 230 NATURAL | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® B |
| Titalon® 1100ST | Titan Plastics Compounds Co., Ltd. | Nylon 6 | Titalon® |
| Wondel® P PN0W | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| Geon™ Vinyl Flexible XV 1197 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| POLYFLAM® HSF 33 E | A. Schulman Europe | PS (GPPS) | POLYFLAM® |