Petrothene® NA443 (Blown)
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sM3sMo_Petrothene-NA443-Blown-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETROTHENE NA 443 is a series of low density/EVA copolymer resins for high impact/high clarity packaging applications. NA 443 exhibits excellent processability and good balance of optics, stiffness and strong heat sealing characteristics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.927 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 4.5 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 32 µm | 138 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm | 124 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm | 27.6 | MPa | ASTM D882 |
| TD : Yield, 32 µm | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm | 350 | % | ASTM D882 |
| TD : Broken, 32 µm | 550 | % | ASTM D882 |
| Dart Drop Impact (32 µm) | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength - MD (32 µm) | 140 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 88.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 166 - 193 | °C |
| Extrusion instructions |
|---|
| NA 443 has excellent drawdown characteristics that yield outstanding output rates. Optimum properties are obtained over a broad range of extrusion conditions at melt temperatures between 330°-380°F (166°-194°C), and a blow-up ratio between 1.7-3.0:1. Using proper techniques and equipment, NA 443 can be drawn to 1.0 mil (19 microns) at commercial production rates. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safron® R101-01NU | Safripol (PTY) LTD | PP Random Copolymer | Safron® |
| Clariant Nylon 6/6 R66G33-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| ESTOPLAST XU 400 NN11 | Ester Industries Ltd. | Nylon, Unspecified | ESTOPLAST XU |
| HiFill® PA6 GF43 LE | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Plaskon SMT-B-1FX | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |